Iranian Journal of Polymer Science and Technology 10163255 23 1 2013 01 28 Crosslinkers of Different Types in Precipitation Polymerization of Acrylic Acid Crosslinkers of Different Types in Precipitation Polymerization of Acrylic Acid 75 84 649 10.22063/jipst.2013.649 FA H. Eshaghi G. Bagheri Marandi H. Boohendi M.J. Zohuriaan-Mehr K. Kabiri Journal Article 2013 01 28 Crosslinked poly(acrylic acid)s were prepared using two types of crosslinker by precipitation polymerization method in a binary organic solvent. N,N’-methylenebisacrylamide (MBA) and polyethylene glycol dimethacrylate (PEGDMA-330) were used as low-molecular weight and long-chain crosslinkers, respectively. The effect of various types of crosslinkers on polymer characteristics (i.e., gel content, equilibrium swelling, glass transition temperature, and rheological properties) was investigated. Maximum amount of viscosity was obtained by using long-chain crosslinker. The Flory-Rehner equation and rubber elasticity theory were used to discuss the network structure of polymer. It was observed that, the glass transition temperature (Tg) of the synthesized polymer containing PEGDMA-330 is higher than that of polymer containing MBA. Apparent and rotational viscosity were used to determine the optimal crosslinker type. In addition, the consistency<br />coefficient (m) and flow behavior index (n) parameter of Ostwald equation were investigated as well. Crosslinked poly(acrylic acid)s were prepared using two types of crosslinker by precipitation polymerization method in a binary organic solvent. N,N’-methylenebisacrylamide (MBA) and polyethylene glycol dimethacrylate (PEGDMA-330) were used as low-molecular weight and long-chain crosslinkers, respectively. The effect of various types of crosslinkers on polymer characteristics (i.e., gel content, equilibrium swelling, glass transition temperature, and rheological properties) was investigated. Maximum amount of viscosity was obtained by using long-chain crosslinker. The Flory-Rehner equation and rubber elasticity theory were used to discuss the network structure of polymer. It was observed that, the glass transition temperature (Tg) of the synthesized polymer containing PEGDMA-330 is higher than that of polymer containing MBA. Apparent and rotational viscosity were used to determine the optimal crosslinker type. In addition, the consistency<br />coefficient (m) and flow behavior index (n) parameter of Ostwald equation were investigated as well. http://jips.ippi.ac.ir/article_649_aeafbe20b4f723a55c26e2bd22e3f0d3.pdf