Effect of Surface Modification of Nanosilica on the Viscoelastic Properties of Its Polystyrene Nanocomposite

Mortezaei, M.; Navid Famili, M.H.; Kokabi, M.

doi:10.22063/jipst.2008.724

Effect of Surface Modification of Nanosilica on the Viscoelastic Properties of Its Polystyrene Nanocomposite

Document Type : Research Paper

Authors

M. Mortezaei

M.H. Navid Famili

M. Kokabi

10.22063/jipst.2008.724

Abstract

The preparation and characterization of the vinyltriethoxysilane-modified silica nanoparticles were investigated. Also the surface tension of polystyrene, native (hydrophilic) silica and silane-modified (hydrophobic) silica were determined. Two kinds of polystyrene/silica (treated and non-treated) nanocomposites were prepared with different filler loadings by solution method. Their viscoelastic properties were studied by dynamic stress controlled rotary shear rheometer. Solid-like response of polystyrene/native silica nanocomposites were observed in the terminal zone. Solid inclusions
increase the storage modulus more than the loss modulus, hence decrease the material damping. By increasing filler volume fraction, the particles tend to agglomerate and build clusters. The presence of clusters increases the viscosity, the moduli and the viscoelastic non-linearity of the composites.
Treating the filler surface reduces its tendency to agglomerate as well as the adhesion between the particles and the polystyrene, leading to lower viscosity and interfacial slippage. Also the loss modulus peak is affected significantly by the particle surface area and its surface property in silica-filled polystyrene, which corresponds to its glass transition.

Keywords

nanosilica

Polystyrene

surface modification

viscoelastic properties

glass transition