Synthesis of Plate-Like Nanoalumina and Its Effect on Gas Permeability of Carbon Fiber Epoxy Composite

Document Type : Research Paper

Authors

Polymer Engineering Department, Faculty of Chemical Engineering, Tarbiat Modares University, P.O. Box: 14115-114, Tehran, Iran

Abstract

In recent years considerable efforts have been made to develop gas impermeable polymer systems. Compared with metal system counterparts they have advantages such as low density and production costs. The most important challenge in development of impermeable polymer systems is to reduce their gas permeability by proper selection of system composition and process conditions. In this work, nanoparticles were initially synthesized using Al (NO3)3•9H2O and sodium dodecyl sulfate as a structure-directing agent via hydrothermal method and a plate-like structure was characterized by FESEM and EDAX analyses. In the second step, epoxy/plate-like nanoalumina nanocomposites and epoxy-carbon fiber composites containing 1, 2.5, and 5 wt% nanoalumina were prepared. The effect of nanoparticle loading level on permeability of nitrogen, argon, and carbon dioxide in epoxy/plate-like nanoalumina nanocomposites was investigated. It was observed that the permeability of epoxy/plate-like nanoalumina nanocomposites toward nitrogen, argon, and carbon dioxide gases reduced 83%, 74%, and 50%, respectively. It was deduced that the permeability reduction was clearly associated with the diameter of gas molecules. Generally speaking, the results showed that the incorporation of plate-like nanoalumina particles significantly reduced the gas permeability. Also, carbon dioxide gas permeability of carbon fiber epoxy composites containing plate-like nanoalumina was investigated to show the effect of ingredients on the gas permeability of the system. The results indicated that carbon dioxide gas permeability of epoxy carbon fiber composite containing 5 wt% of plate-like nanoalumina was totally reduced 84%.

Keywords

References

1.Choi S. and Sankar B.V., Gas Permeability of Various Graphite/Epoxy Composite Laminates for Cryogenic Storage Systems, Composites, Part B, 39, 782-791, 2008.
2.Sun L., Boo W.J., Clearfield A., Sue H.J., and Pham H.Q., Barrier Properties of Model Epoxy Nanocomposites, J. Membr. Sci., 318, 129-136, 2008.
3.Lai M. and Kim J.K., Effects of Epoxy Treatment of Organoclay on Structure, Thermo-Mechanical and Transport Properties of Poly(ethylene terephthalate-co-ethylene naphthalate)/Organoclay Nanocomposites, Polymer, 46, 4722-4734, 2005.
4.Chaiko D.J. and Leyva A.A., Thermal Transitions and Barrier Properties of Olefinic Nanocomposites, Chem. Mater., 17, 13-19, 2005.
5.Meneghetti P. and Qutubuddin S., Synthesis, Thermal Properties and Applications of Polymer-Clay Nanocomposites, Thermochim. Acta, 442, 74-77, 2006.
6.Picard E., Vermogen A., Gerard J.F., and Espuche E., Barrier Properties of Nylon 6 -Montmorillonite Nanocomposite Membranes Prepared by Melt Blending: Influence of the Clay Content and Dispersion State: Consequences on Modelling, J. Membr. Sci., 292, 133-144, 2007.
7.Ogasawar T., Ishida Y., Ishikawa T., Aoki T., and Ogura T., Helium Gas Permeability of Montmorillonite/Epoxy Nanocomposites, Composites, Part A, 37, 2236-2240, 2006.
8.Osman M., Mittal V., Morbidelli M., and Suter U., Epoxy-Layered Silicate Nanocomposites and Their Gas Permeation Properties, Macromolecules, 37, 7250-7257, 2004.
9.Mousavi S.A., Sadeghi M., Roosta-Azad R., and Ahamadi-Roshan M., Study of Morphology and Gas Permeability in Ethylene/Vinyl Acetate Membrane Prepared via Thermal Phase Inversion, Iran. J. Polym. Sci. Thechnol. (Persian), 1, 25-36, 2007.
10.Choudalaki G. and Gotsis A.D., Free Volume and Mass Transport in Polymer Nanocomposites, Curr. Opin. Colloid Interface Sci., 17, 132-140, 2012.
11.Cui Y., Kundalwal S.I., and Kumar S., Gas Barrier Performance of Graphene/Polymer Nanocomposites, Msc Thesis, Massachusetts Institute of Technology, Cambridge, 2009.
12.Mittal V., Epoxy-layered Silicate Nanocomposites: Effect of Cross-linking Amines and Fillers on Curing, Morphology and Oxygen Permeation, J. Reinforc. Plast. Compos., 31, 739-747, 2012.
13.Choudalakis G. and Gotsis A.D., Permeability of Polymer/Clay Nanocomposites: A Review, Eur. Polym. J., 45, 967-984, 2009.
14.Lim S.H., Zeng K., and He C., Preparation, Morphology and Mechanical Properties of Epoxy Nanocomposites with Alumina Fillers, Int. J. Mod. Phys. B., 24, 136-147, 2010.
15.Nagarajan R., Molecular Packing Parameter and Surfactant Self-assembly: The Neglected Role of the Surfactant Tail, Langmuir, 18, 31-38, 2002.
16.Franks G.V. and Gan Y., Charging Behavior at the Alumina-Water Interface and Implications for Ceramic Processing, J. Am. Ceram. Soc., 90, 3373-3388, 2007.
17.Nielsen L.E., Models for the Permeability of Filled Polymer Systems, J. Macromol. Sci. Chem., 1, 929-942, 1967.
18.Tremblay P., Savard M., Vermette J., and Paquin R., Gas Permeability, Diffusivity and Solubility of Nitrogen, Carbon Dioxide and Formaldehyde in Dense Polymeric Membranes Using a New On-line Permeation Apparatus, J. Membr. Sci., 282, 245-256, 2006.
Iranian Journal of Polymer Science and Technology
Volume 30, Issue 1 - Serial Number 147
March and April 2017
Pages 43-51

Files

Share

How to cite

Statistics